Grain-oriented ferroelectric bismuth titanate thin film prepared from acetate precursor

1996; Elsevier BV; Volume: 39; Issue: 1 Linguagem: Inglês

10.1016/0921-5107(95)01432-2

1873-4944

Yanxia Lu, D. Hoelzer, Walter A. Schulze, Bruce A. Tuttle, B. G. Potter,

Photorefractive and Nonlinear Optics

Bismuth titanate (Bi4Ti3O12) thin films were fabricated by a spin coating deposition and rapid thermal processing (RTP) technique. The acetate-derived solution for deposition was synthesized by blending dissolved bismuth acetate in aqueous acetic acid and then adding titanium acetate. A series of electrically insulating, semiconducting and conducting substrates were evaluated for Bi4Ti3O12 films deposition. X-ray diffraction indicated that the initial crystallization temperature of the Bi4Ti3O12 films was 500 °C or less; a 700 °C crystallization treatment was used to obtain single phase films. The Bi4Ti3O12 film crystallographic orientation is shown to depend on three factors: substrate type; number of coating layers; and thermal processing. While preferred c-direction orientation was observed for films deposited on silver foil substrates, preferred a-direction orientation was obtained for films deposited on both Si and Pt coated Si wafers. The films were dense, smooth, crack-free and had grain sizes ranging from 20 to 400 nm. Film thickness and refractive index were determined using a combination of ellipsometry, waveguide refractometry and TEM techniques. The refractive index is close to the value of single crystal BIT.