Effect of different retanning systems on surface properties of leather

2007; American Leather Chemists Association; Volume: 102; Issue: 4 Linguagem: Espanhol

0002-9726

Swarna V. Kanth, A. Ipe, Balaraman Madhan, R. Venba, A. Dhathathreyan,

Collagen: Extraction and Characterization

The present work attempts to analyze the surface properties of crust leathers processed using different syntans of the type phenol-naphthalene formaldehyde condensate, phenol formaldehyde, melamine formaldehyde, gluteraldehyde, styrene maleic anhydride, acrylic polymer, sulphone and heterocyclic N-methylol. Contact angles of liquid drops on the leather surfaces have been used to evaluate surface energy, acidity, basicity, polarity, work of adhesion and surface roughness. The surface energy component showed that the control crust leather without retanning is practically monopolar basic with ?S- = 13.02 mN/m. Acrylic polymer retanned crust leather exhibited high basic character (?S- = 33.15 mN/m), while phenol formaldehyde retanned crust leather had the least values (?S- = 1.03 mN/m). The surface behavior towards rub fastness and adhesion of finish has been significantly altered by the retanning systems in leathers and showed a good correlation with the surface properties like surface charge, polarity, roughness and work of adhesion. RESUMENEl presente trabajo procura analizar las propiedades superficiales de los cueros semi-terminados procesados usando diversos sintanes del tipo condensado del fenol-naftalina formaldehido, fenol formaldehido, melamina formaldehido, glutaraldehido, anhidrido estireno-maleico, polimero acrilico, sulfonico y heterociclico de N-Metilol. Los angulos del contacto de gotas liquidas en la superficie del cuero se han utilizado para evaluar la energia superficial, la acidez, la basicidad, la polaridad, la adherencia y la aspereza de la superficie. El componente de energia de la superficie demostro que el cuero semi-terminado de control sin recurtido es practicamente monopolar basico con ?S- = 13.02 mN/m. El cuero semi-terminado recurtido con polimeros acrilicos exhibio un caracter altamente basico (?S- = 33.15 mN/m), mientras que el cuero semi-terminado recurtido con formaldehido fenolico tuvo los menores valores (?S- =1.03 mN/m). El comportamiento superficial en cuanto a las solideces al frote y la adherencia del acabado ha sido alterado perceptiblemente por los sistemas recurtido en los cueros y demostro una buena correlacion con las propiedades de la superficie como la carga superficial, la polaridad, la aspereza y la adherencia.