Current-perpendicular-to-plane giant magnetoresistance in spin-valve structures using epitaxial Co2FeAl0.5Si0.5/Ag/Co2FeAl0.5Si0.5 trilayers
2008; American Institute of Physics; Volume: 93; Issue: 12 Linguagem: Inglês
10.1063/1.2990647
ISSN1520-8842
AutoresT. Furubayashi, Komomo Kodama, Hiroaki Sukegawa, Y. K. Takahashi, K. Inomata, K. Hono,
Tópico(s)Magnetic properties of thin films
ResumoA current-perpendicular-to-plane giant magnetoresistance (CPP-GMR) spin valve using epitaxial layers of Co2FeAl0.5Si0.5 (CFAS) Heusler alloy as ferromagnetic electrodes is reported. A multilayer stack of Cr/Ag/CFAS/Ag/CFAS/Co75Fe25/Ir22Mn78/Ru was deposited on a MgO (001) single crystal substrate. Epitaxial growth of the Cr, Ag, and CFAS layers in the (001) orientation up to the top CFAS layer was confirmed. Large MR ratios of 6.9% at room temperature and 14% at 6 K were observed for the CPP-GMR device. High spin polarization of epitaxial CFAS is the possible reason for high MR ratios.