Portal de Periódicos da CAPES

VIDRIADO CON LÁSER DE Nd:YAG SOBRE AZULEJOS RECUBIERTOS DE BARNICES DE COBALTO CON FRITA BORÁCICA Y SIN FRITA (Nd:YAG LASER ENAMELING ON GLAZED TILES COATED WITH COBALT VARNISHES WITH AND WITHOUT BORAX FRIT/ VIDRADO COM LASER DE Nd:YAG SOBRE AZULEJOS RECO

2014; EIA University; Volume: 7; Issue: 13 Linguagem: Espanhol

10.24050/reia.v7i13.493

2463-0950

Maryory Astrid Gómez Botero, José William Restrepo,

3D Surveying and Cultural Heritage

Las industrias de materiales ceramicos y arquitectonicos emplean diferentes tecnicas de marcado con dos aplicaciones clasicas, para identificacion y decoracion de piezas elaboradas. La utilizacion de tecnicas laser para estos propositos se viene implementando de forma creciente, debido a las ventajas que presenta respecto al horneado convencional: la concentracion del calor solo en la zona irradiada, lo que conlleva un menor consumo de energia sin afectar significativamente el resto de la pieza; se obtienen patrones graficos de alta resolucion espacial; permite introducir cambios durante el proceso sin requerir largas paradas, y la generacion de residuos es minima o casi nula. En este estudio se presentan los resultados obtenidos en el vidriado con laser Nd:YAG (l=1064 nm) sobre las superficies esmaltadas de azulejos, las cuales fueron previamente recubiertas con pigmento ceramico negro de cobalto y un barniz constituido por este mismo pigmento y frita boracica. Con el laser operando en modo continuo (CW), se marcaron una serie de lineas, cuyo ancho y profundidad evidenciaron una dependencia directa, con la variacion de la potencia y velocidad de desplazamiento del haz laser sobre la superficie del azulejo. Finalmente estas lineas vidriadas fueron analizadas por microscopia optica, espectroscopia de dispersion de energia (EDS) y difraccion de rayos X. Abstract: Ceramic and architectonic materials industries employ different marking techniques with two classical applications, identification and decoration of manufactured objects. Laser techniques using for these proposes are been implemented in growing way, due to theirs advantages with regard to the conventional baking such as: heat is concentrated only on the radiated zone which involves a smaller energy consumption without affecting significantly the rest of the piece; graphic patterns with of highly spatial resolution are obtained; it permits to introduce changes during the process no requiring long stops and low or almost none generation of residues. In this study the results obtained from Nd:YAG (l=1064 nm) laser glazing on the enameled surfaces of glazed tiles, which were previously covered with cobalt black pigment and an enamel constituted with this same pigment and borax frit, are presented. With the laser operating in continuous wave (CW), a series of lines were marked, whose width and depth showed a direct dependence with the variation in the power and scan speed of the laser beam on the glazed tile surface. Finally, these glazed lines were characterized by optical microscopy, energy dispersion spectroscopy (EDS), and X- ray diffraction (XRD). Sumario: As industrias de materiais cerâmicos e arquitetonicos empregam diferentes tecnicas de marcado com duas aplicacoes classicas, para identificacao e decoracoes de pecas elaboradas. A utilizacao de tecnicas laser para estes propositos se vem executando de forma crescente, devido as vantagens que apresenta respeito ao assado convencional: concentracao do calor so na zona irradiada, o que comporta um menor consumo de energia sem afetar significativamente o resto da peca; obtem-se patroes graficos de alta resolucao espacial; permite introduzir mudancas durante o processo sem requerer longas paradas, e a geracao de residuos e minima ou quase nula. Neste estudo se apresentam os resultados obtidos no vidrado com laser Nd:YAG (l=1064 nm), sobre as superficies esmaltadas de azulejos, as quais foram previamente recobertas com pigmento preto de cobalto e um verniz constitudo com este mesmo pigmento e frita boracica. Com o laser operando em modo continuo (CW), marcaram-se uma serie de linhas, cujo largo e profundidade evidenciaram uma dependencia direta com a variacao da potencia e velocidade de deslocamento do feixe laser sobre a superficie do azulejo. Finalmente, estas linhas vidradas foram analisadas por microscopia optica, espectroscopia de dispersao de energia (EDS) e difracao de raios X.