Magnetic properties of ferromagnetic γ-Fe films on Cu (111)

1978; Wiley; Volume: 45; Issue: 1 Linguagem: Inglês

10.1002/pssa.2210450120

1521-396X

W. Kümmerle, U. Gradmann,

Magnetic Properties and Applications

Epitaxial f.c.c. γ-Fe-films on Cu (111) with a well-defined structure are measured magnetometrically. Layer-grown as well as island-grown films prepared with a film thickness between 3 and about 85 Å, are found to be ferromagnetic with a magnetic moment of (0.58 ± 0.13) μB/atom. The temperature dependence of the anisotropy field differs fundamentally for layer- and islandgrown films. The existence of ferromagnetic γ-Fe-films, which seems to be controversal to the antiferromagnetism of γ-Fe-precipitates, can be explained by the epitaxial expansion of the lattice parameter and will be discussed in terms of different concepts of the magnetic order in γ-Fe. Epitaktische k.f.z.-γ-Fe-Filme auf Cu (111) mit wohldefinierter Struktur werden magnetometrisch vermessen. Im untersuchten Schichtdickenbereich von 3 bis ca. 85 Å sind diese Filme ferromagnetisch mit einem magnetischen Moment von (0,58 ± 0,13) μB/Atom, sowohl für flächenhafte als auch für Inselschichten. Die Anisotropiefelder dagegen zeigen für flächenhafte und Inselscher γ-Fe-Filme im Gegensatz zu den antiferromagnetischen γ-Fe-Ausscheidungen wird auf die epitaktisch gedehnte Gitterkonstante zurückgeführt und im Rahmen verschiedener Modelle der magnetischen Ordnung des γ-Fe diskutiert.