Hardened portland cement pastes of low porosity IV. Surface area and pore structure

1972; Elsevier BV; Volume: 2; Issue: 5 Linguagem: Inglês

10.1016/0008-8846(72)90112-3

1873-3948

I. Odler, Julius Hagymassy, E.E Bodor, Marvin Yudenfreund, Stephen Brunauer,

Grouting, Rheology, and Soil Mechanics

This paper deals with the total surface areas, total pore volumes, and the distribution of pore surface and pore volume in pores of different sizes of 25 low-porosity pastes. A Type II clinker was ground with two grinding aids: diethyl carbonate and Reax 70. The water-cement ratios were 0.2 and 0.3. The hydration temperatures were 5°, 25°, and 50°C. Nitrogen adsorption isotherms at -196°C and water vapor adsorption isotherms at 25°C were used for the surface area and pore structure determinations. The methods used in the analyses of micropores and wider pores were those developed by Brunauer and his coworkers. Für 25 Pasten mit niedriger Porosität wurden die Gesamtoberfläche, das Gesamtporenvolumen und die Verteilung von Porenoberfläche und Porenvolumen in Poren verschiedener Gröβe untersucht. Ein Klinker vom Typ II wurde mit zwei Mahlhilfen gemahlen: Diäthylkarbonat und Reax 70. Die Wasser-Zement Werte waren 0.2 und 0.3, die Hydratationstemperaturen 5°, 25° and 50°C. Zur Bestimmung der Oberflächen und der Porenstruktur wurden Adsorptions-Isothermen von Stickstoff bei -196°C und von Wasserdampf bei 25°C benutzt. Für die Analyse von Mikroporen und grösseren Poren wurden die von Brunauer und Mitarbeitern entwickelten Methoden angewandt.