High strength cold rolled steel sheets with a high drawability

1977; Elsevier BV; Volume: 29; Issue: 1 Linguagem: Francês

10.1016/0025-5416(77)90144-6

1873-4928

Y. Meyzaud, P. Parniere,

Metallurgy and Material Forming

After a short review of the properties required from high yield strength, cold-rolled steel sheets, a description is given of the fabrication process leading to high yield strength and high mean strain ratio with the use of copper-bearing low carbon steels. Results obtained from laboratory-made sheets are presented; they concern mainly the evolution of the annealing texture with the composition and the coiling temperature, and the influence of the hardening treatment on the strength, strain ratio and strain-hardening coefficient. The determination of the tensile mechanical properties has been completed with deep drawing experiments (FUKUI test). The formability of these sheets is fairly high, but the forming procedures should be designed to avoid, as much as possible, deformation by stretching and to use essentially deformation by drawing. Après un bref rapple des propriétés requises de tôles minces à haute limite d'élasticité, nous décrivons le procédé de fabrication permettant d'obtenir des tôles à coefficient d'anisotropie r et limite d'élasticité élevés à partir d'aciers extra doux contenant du cuivre. Nous présentons ensuite les résultats obtenus sur des tôles préparées en laboratoire, concernant, en particulier, l'évolution de la texture de recuit avec la composition et la température de bobinage, et l'influence du traitement de durcissement sur le coefficient d'écrouissage. La détermination des propriétés mécaniques en traction a été complétée par des essais d'emboutissage (essai FUKUI). L'emboutissabilité de ce type de tôles peut ětre tout à fait convenable à condition d'éviter autant que possible les déformations en expansion pour faire appel essentiellement au rétreint.