Mechanical behaviour of fresh concrete

1981; Elsevier BV; Volume: 11; Issue: 3 Linguagem: Francês

10.1016/0008-8846(81)90105-8

1873-3948

Alex Alexandridis, N. J. Gardner,

Concrete and Cement Materials Research

The shear strength characteristics of fresh concrete were studied through the use of a triaxial compression apparatus on concrete cylinders 100 mm in diameter and 200 mm high at 21°C and 4°C for set times ranging from 40 minutes to 160 minutes. The test results were analyzed by the shear strength theories of Mohr-Coulomb and Rowe for each time-temperature combination. The angle of internal friction was found to be a constant property of the mix in the range of 37° to 41° for a 10% failure strain when analyzed by Mohr-Coulomb. Rowe's analysis gave friction angles of 18° to 21° for a 10% failure strain. Both theories indicate that the cohesion of fresh concrete is initially zero and increases with set time. La résistance au cisaillement du béton frais a été étudiée avec l'aide d'un appareil triaxial sur des échantillons de 100 mm de diamétre par 200 mm en grandeur à 21°C et 4°C pour une durée de 40 minutes à 160 minutes. Par la suite les résultats ont été analysés employant les théories de Mohr-Coulomb et Rowe et ont été exprimés comme les deux paramètres de cohésion et de frottement pour chaque combinaison de température et de durée. On a déduit que l'angle de frottement était une propriété constante du mélange et résidait entre 37° et 41° pour une déformation finale de 10% utilisant la théorie de Mohr-Coulomb. L'analyse de Rowe a donné des angles de frottement de 18° à 21° pour une déformation finale de 10%. Les deux théories ont indiqué que la cohésion était initialement zéro et qu'elle s'était agrandit avec le temps.