Effectiveness factors in a three-phase slurry reactor: the reduction of crotonaldehyde over a palladium catalyst
1972; Elsevier BV; Volume: 27; Issue: 11 Linguagem: Inglês
10.1016/0009-2509(72)87061-1
ISSN1873-4405
Autores Tópico(s)Catalysis and Hydrodesulfurization Studies
ResumoRate measurements are described of the reduction of liquid crotonaldehyde by hydrogen in a slurry reactor using palladium deposited on the surface and a porous γ-alumina. Measurements were made at ambient pressure and temperatures between 30° and 70°C using: (a) 316 in. cylindrical catalyst pellets and (b) powdered pellets for which the mean particle size was 30 μ. The effectiveness factor for the commercial palladium catalyst is calculated to be ca. 0.1 with an average tortuosity factor of 1·6. Les auteurs décrivent les mesures du taux de réduction de l'aldéhyde liquide de corton par l'hydrogène dans un réacteur à suspensions, en utilisant du palladium déposé sur la surface d'une alumine γ poreuse. Les mesures ont été effectuées sous une pression ambiante et à des températures allant de 30°C à 70°C, en utilisant: (a) des grains de catalyseur cylindriques de 0,47 cm et (b) des grains de poudre dont la taille moyenne des particules était de 30 μ. Le facteur d efficacité du catalyseur commercial au palladium est d'environ 0,1 avec un facteur de tortuosité moyenne de 1,6. Es werden Geschwindigkeitsmessungen bei der Reduktion von flüssigem Crotonaldehyd durch Wasserstoff in einem Schlammreaktor unter Verwendung von an der Oberfläche poröser γ Tonerde abgelagertem Palladium beschrieben. Es wurden Messungen durchgeführt bei Umgebungstemperatur und bei Temperaturen zwischen 30°C und 70°C unter Verwendung von: (a) 316″ zylindrischen Katalysatorteilchen und (b) pulverisierten Teilchen, bei welchen die durchschnittliche Korngrösse 30 μ war. Als Wirksamkeitsfaktor für de n handelsmässigen Palladiumkatalysator wurde ca. 0,1 errechnet bei einem durchschnittlichen Krümmungsfaktor von 1,6.
Referência(s)