Nb/Nb oxide/Pb-alloy Josephson tunnel junctions

1981; IEEE Magnetics Society; Volume: 17; Issue: 1 Linguagem: Inglês

10.1109/tmag.1981.1060970

ISSN

1941-0069

Autores

S. I. Raider, R.E. Drake,

Tópico(s)

Surface and Thin Film Phenomena

Resumo

A procedure is described for fabricating thin film Nb/Nb oxide/Pb-alloy Josephson tunnel junctions that satisfies the principal requirements for integrated circuit design and fabrication. A deposited Nb film, evaporated from an e-gun heated source, was patterned by chemical etching to form a base electrode. A junction was completed by plasma etching and plasma oxidizing the Nb junction area to form a tunnel barrier and by depositing a Pb alloy counterelectrode. Josephson tunnel junctions with Nb/Nb oxide/Pb-Au-In structures were prepared with low excess subgap currents in the current-voltage (I-V) curve and with reproducible and stable I-V characteristics. Variations in junction current density from run-run were ± 15%. Seven 3-junction interferomeeters out of a population of 50,000 were shorted (99.99% yield) for causes not immediately attributable to photoresist-related defects. No changes in Josephson current were detected after thermal cycling 17,000 interferometers 1,800 × between room temperature and 4.2°K, after storing them for 2 years at 5°C, or after annealing 5,000 interferometers for 4.5 hours at 70°C.

Referência(s)
Altmetric
PlumX