Effect of large additions of Cd, Pb, Cr, Zn, to cement raw meal on the composition and the properties of the clinker and the cement

1996; Elsevier BV; Volume: 26; Issue: 3 Linguagem: Francês

10.1016/s0008-8846(96)85025-3

1873-3948

Michel Murât, F. Sorrentino,

Materials Engineering and Processing

The addition of important quantities of Cd, Pb, Cr, Zn to raw meals of Portland and calcium aluminate cement modifies the mineralogical composition and the properties of the final cement. Portland cement can absorb a large amount of Cd, and Zn. This absorption leads to an increase of setting time and a decrease of strengths of the cement. It also can trap chromium with a short setting time and high strengths. Calcium aluminate cements easily trap Cd and Cr with a delayed setting and good strength but also Pb with normal setting time and strengths. Large quantities of zinc oxide have a deleterious effect on calcium aluminate strengths. L'addition d'importantes quantités de Cd, Pb, Cr, Zn au cru de ciment Portland et alumineux modifie la composition mineralogique et les propriétés du ciment final. Le ciment Portland peut absorber de grandes quantités de cadmium et de zinc. cette absorption conduit à une augmentation du temps de prise et une diminution des résistances du ciment. Il peut aussi piéger le chrome avec un temps de prise plus court et de hautes résistances. Les ciments à base d'aluminates de calcium piégent facilement Cd et Cr avec un temps de prise plus long et de bonnes résistances, mais aussi Pb avec un temps de prise et des résistances normales. De grandes quantités d'oxyde de zinc ont une action néfaste sur les résistances des ciments d'aluminates de calcium.