Containerless undercooling and solidification in drop tubes
1981; Elsevier BV; Volume: 51; Issue: 1 Linguagem: Inglês
10.1016/0022-0248(81)90007-5
ISSN1873-5002
AutoresL. L. Lacy, Michael B. Robinson, T. J. Rathz,
Tópico(s)Solidification and crystal growth phenomena
ResumoA containerless low-gravity environment, produced within a 32 m drop tube apparatus, has been used to undercool and solidify metals, alloys or glasses by eliminating crucible induced nucleation processes. Niobium droplets with diameters in the range of 2 to 5 mm have been undercooled by 525 K which corresponds to the maximum undercooling reported by Turnbull and others on fine dispersions of low melting point metals. Solidification at large undercooling resulted in single crystalline spheres with the formation of interdendritic shrinkage channels on the sample surface rather than interior shrinkage cavities. The grain refinement as observed for Ni samples undercooled and solidified in fused silica crucibles does not occur in free-falling drops of Nb. A calculated solidification speed of undercooled Nb is compared to Ni. A solidification speed of 320 m/s is found for the Nb drops. This solidification speed is greater than or comparable to the solidification speeds calculated in splat cooled samples. Thus, a drop tube apparatus can be useful in the preparation and study of high temperature metastable compounds or alloys in bulk form.
Referência(s)