Damping of ferromagnetic resonance in NiFe alloys

1976; Wiley; Volume: 35; Issue: 1 Linguagem: Inglês

10.1002/pssa.2210350113

1521-396X

Dennis Bastian, E. Biller,

Magnetic Properties of Alloys

From linewidth data of bulk (110) NiFe alloy single crystals (100 to 45 wt% Ni) at 19.5 and 26 GHz Landau-Lifshits damping parameters were derived, which, except for 100% Ni, increase with temperature between — 196 °C and the Curie point. The λ values of the alloys are found to be considerably lower than for pure Ni. For 75% Ni, λ shows a very pronounced decrease with increasing degree of order. The λ dependence on frequency, temperature, alloy composition, and state of order is in qualitative agreement with a relaxation model on the basis of spin—orbit effects within a band picture proposed by Kamberský. Aus Linienbreitenmessungen an kompakten (110)-Einkristallen der NiFe-Legierungsreihe (100 bis 45 Gew% Ni) bei 19,5 und 26 GHz werden Landau-Lifshits-Dämpfungsparameter λ ermittelt, die außer bei 100% Ni, zwischen — 196 °C und dem Curiepunkt mit der Temperatur zunehmen. Die bei den Legierungen gefundenen λ-Werte sind wesentlich niedriger als bei reinem Ni. Bei 75% Ni zeigt λ eine starke Abnahme mit zunehmendem Ordnungsgrad. Die Abhängigkeit von λ von Frequenz, Temperatur, Legierungszusammensetzung und Ordnungsgrad ist in qualitativer Übereinstimmung mit einem Relaxationsmodell, welches von Kamberský auf der Grundlage von Spin—Bahn-Effekten im Rahmen einer Bandvorstellung vorgeschlagen wurde.