Order-disorder transition and structure of the ordered vacancy compound Nb 6 C 5 : powder neutron diffraction studies

1985; IOP Publishing; Volume: 18; Issue: 4 Linguagem: Inglês

10.1088/0022-3719/18/4/012

1747-3802

Jean-Pierre Landesman, A. Nørlund Christensen, C.H. de Novion, N. Lorenzelli, P. Convert,

Inorganic Chemistry and Materials

High-resolution neutron diffraction studies of NbC0.83 powders are described. In a first set of experiments the order-disorder transition was studied by measuring the integrated Bragg intensities. A first-order transition is observed around 1025+or-5 degrees C on heating, which shows a hysteresis. In a second set of experiments, a profile refinement method was used to get information on the crystal structure of a well ordered Nb6C5 sample. The V6C5-type trigonal superstructure previously proposed was confirmed (rather than the V6C5 monoclinic form). A shift of the niobium atoms ( approximately=0.05 AA) away from their first-nearest-neighbour vacant site, towards a first-nearest-neighbour occupied site (trans to the former) is found.