Mean velocity of edge and screw dislocation groups in neutron-irradiated copper single crystals

1978; Wiley; Volume: 49; Issue: 2 Linguagem: Inglês

10.1002/pssa.2210490204

1521-396X

R. Rodloff, H. Neuhäuser,

Nuclear materials and radiation effects

During deformation of n-irradiated Cu single crystals (n-dose 2.6 × 1018 cm−2) in the yield region at room temperature the development of slip bands on several surfaces around the crystal is recorded by high-speed cinematography. From microphotometric evaluation of the films (rate of growth of slip bands in length and in height) the mean velocity of dislocation groups, the distances of dislocations in the moving groups, and their average angle to the crystal surface is obtained. Velocities of screw (v⊙) and edge (v⊥) dislocation groups at different surfaces indicate an effect of the surface (“image forces”). An increase of deformation rate by a factor of 21 causes an increase of v⊙ and v⊥ by only a factor of six. Without surface effects v⊙/v⊥ ≈︁ 4. Während der Verformung von n-bestrahlten Cu-Einkristallen (n-Dosis 2,6 × 1018 cm−2) im Fließbereich bei Raumtemperatur wird die Entwicklung von Gleitbändern auf mehreren Flächen rund um den Kristall mit Hochfrequenz-Kinematographie registriert. Die mikrophotometrische Auswertung der Filme (Wachstumsgeschwindigkeit der Gleitbänder in die Länge und Höhe) ergibt die mittlere Geschwindigkeit der Versetzungsgruppen, die Versetzungsabstände in bewegten Gruppen und ihren mittleren Winkel gegen die Kristalloberfläche. Die Geschwindigkeiten von Schrauben- und Stufenversetzungsgruppen (v⊙ bzw. v⊥) lassen einen Einfluß der Oberfläche („Bildkräfte”︁) erkennen. Eine Zunahme der Dehngeschwindigkeit um den Faktor 21 hat eine Zunahme von v⊙ und v⊥ nur um den Faktor sechs zur Folge. Ohne Oberflächeneffekt ist v⊙/v⊥ ≈︁ 4.