Low stacking-fault density in ZnSe epilayers directly grown on epi-ready GaAs substrates without GaAs buffer layers
2001; American Institute of Physics; Volume: 78; Issue: 2 Linguagem: Inglês
10.1063/1.1339262
ISSN1520-8842
AutoresSoon‐Ku Hong, E. Kurtz, Ji-Ho Chang, Takashi Hanada, Masaoki Oku, Takafumi Yao,
Tópico(s)Quantum Dots Synthesis And Properties
ResumoWe report a remarkably low stacking-fault density in ZnSe epilayers directly grown on commercial epi-ready GaAs (001) substrates without GaAs buffer layer growth. It is found that proper pregrowth treatments on epi-ready GaAs (001) substrates to obtain clean surfaces are crucial for two-dimensional layer-by-layer growth and suppression of stacking fault generation. Chemical etching using a NH4OH-based solution is found to reduce not only the thickness of the oxide layers but also the ratio of Ga2O3 to As2O3 to about half of that before etching. A clean GaAs (001) surface characterized by a (4×1) reconstruction in the present case is obtained after thermal cleaning followed by Zn pre-exposure. Reflection high-energy electron diffraction intensity oscillations with more than 50 periods are observed even from the very beginning of ZnSe growth on GaAs substrates cleaned as such. The stacking fault density in such a ZnSe layer is in the low-105 cm−2 range.
Referência(s)