Effect of pressure on α-alumina nucleation in boehmite gel

1993; Elsevier BV; Volume: 12; Issue: 4 Linguagem: Inglês

10.1016/0955-2219(93)90099-d

1873-619X

Ladislav Pach, Stefan Kovalík, J. Majling, Jana Kozánková,

Bone Tissue Engineering Materials

The intensity of α-Al2O3 nucleation, in seeded as well as unseeded monolithic boehmite-derived alumina gel, increases after isostatic cold pressing at 1000 and 1500 M Pa. In unseeded gels, a general increase in particle coordination induced by the pressure results in a rise in the number of potential nucleation sites. In seeded gels, a heterogeneous nucleation of α-Al2O3, which takes place on the contact surface of the (γ, δ, θ)-Al2O3 particles with a seed, is a function of the number of these contacts and the pressure applied. In aus Böhmit erhaltenen monolithischen Al2O3-Gelen wird durch kaltisostatisches Pressen (1000–1500 M Pa) die Nukleationsgeschwindigkeit erhöht, sowohl in geimpften als auch ungeimpften Proben. In ungeimpften Gelen wird die Anzahl der potentiellen Keimbildungszentren in Folge der durch den Druck verursachten Erhöhung der Koordinationszahl vermehrt. In geimpften Gelen beginnt die Transformation mit einer heterogenen Nukleation von α-Al2O3 an den Berührungsstellen der (γ, δ, θ)-Al2O3 Partikel mit der Oberfläche des Impfmittels. L'intensité de la nucléation de α-Al2O3 dans les gels compacts dérivès de la boehmite avec et sans germe de Al2O3 augmente aprés une compression isostatique à froid de 1000–1500 M Pa. Dans les gels sans germe, le nombre potentiel de sites de nucléation s'accroit avec l'augmentation de l'indice de coordination des particules sous l'effet de la pression. Dans les gels avec germes, une nucléation hétérogène d'α-Al2O3, qui se produit au niveau de la surface de contact entre les particules d'(γ, δ, θ)-Al2O3 et un germe, est fonction du nombre de ces contacts et de la pression appliquée.