Adsorption of End-Functionalized Poly(ethylene oxide)s to the Poly(ethylene oxide)−Air Interface

1997; American Chemical Society; Volume: 30; Issue: 4 Linguagem: Inglês

10.1021/ma961396v

1520-5835

Zhaohui Su, Dacheng Wu, Shaw Ling Hsu, Thomas J. McCarthy,

Fiber-reinforced polymer composites

Samples with one or both ends of monodisperse poly(ethylene oxide) (PEO) functionalized with perfluorodecanoyl groups (PEOF or PEO2F) were synthesized and blends of these end-capped PEOs with PEOs of the same molecular weight (Mn ∼2000 to ∼16 000 K) were prepared as cast films. As-cast and annealed samples were analyzed by X-ray photoelectron spectroscopy (XPS) and contact angle analysis. XPS analysis was also performed on samples at elevated temperatures (melts). Due to the lower surface energy of the fluorocarbon end groups, the modified PEOs preferentially adsorb to the free polymer surface. The surface concentration of the perfluoroalkyl end groups was measured by XPS which indicates that perfluoroalkyl chain ends adsorb to the polymer surface in a reasonably close-packed fashion (at all molecular weights) and leave a zone depleted of fluorine immediately beneath the highly fluorinated surface region. The dependence of adsorption on temperature was investigated for one sample and adsorption appears to be slightly favored at lower temperatures. PEO2F samples are found to have a slightly higher surface affinity than PEOF of the same molecular weight. There is only a slight effect of molecular weight on surface fluorine content, indicating a "stretched brush" conformation for the higher molecular weight samples.