The habit planes in certain martensitic and nucleation-and-growth transformations

1958; University of Toronto Press; Volume: 6; Issue: 7 Linguagem: Inglês

10.1016/0001-6160(58)90112-3

1878-0768

H. M. Otte, T. B. Massalski,

Microstructure and mechanical properties

The phenomenological theory of martensite formation developed by Wechsler et al. has been used to predict the indices of plane interfaces formed during annealing between grains of α- and β-brass, as well as the habit plane of precipitation of Fe4N, and Fe3P, from α-iron. The implications resulting from the possibility of extending the martensite theory to diffusion controlled “nucleation and growth” transformations are discussed. La théorie de la formation de la martensite développée par Wechsler et al. est utilisée par les auteurs pour prévoir les indices de plan d'interfaces formées au cours du revenu entre des grains de laiton α et β, ainsi que le plan d'habitat de la précipitation de Fe4N et Fe3P à partir de fer α. Les auteurs discutent des conséquences résultant de la possibilité d'extension de la théorie de la martensite aux transformations par nucléation et croissance. Die phänomenologische Theorie der Martensitbildung von Wechsler et al. wird benutzt, um die Indizes der Grenzflächen vorauszusagen, welche sich beim Tempern zwischen Körnern von α- und β-Messing bilden. Auch die Habitusebene der Ausscheidung von Fe4N und Fe4P in α-Eisen wird auf diese Weise bestimmt. Die Folgerungen einer möglichen Anwendung der Martensittheorie auf Keimbildungs-und-Wachstumstransformationen werden diskutiert.