Solution spinning of a semirigid chain polymer forming ultrahigh modulus fibers

1981; Wiley; Volume: 26; Issue: 11 Linguagem: Inglês

10.1002/app.1981.070261112

1097-4628

Barbara Valenti, Giovanni C. Alfonso, A. Ciferri, Paolo Giordani, G. Marrucci,

Nanofabrication and Lithography Techniques

Abstract Single filaments of the polyterephthalamide of p ‐aminobenzylhydrazide (X‐500) were prepared by spinning X‐500 solutions in dimethyl sulfoxide (DMSO) using water as a coagulating agent. The polymer is known for its ability to develop ultrahigh modulus fibers and for having a semirigid chain conformation with a persistence length of ∼50 Å in DMSO. In the latter solvent, molecular rigidity appears to be just below that required for spontaneous formation of a nematic phase. The orientation of the fibers was performed in three different stages: during coagulation (I), in the washing bath following coagulation (II), and during postspinning treatments (III). Corresponding mechanical properties were determined. The results indicate that high elastic modulus (15 GPa) already appears during step I at very moderate pulloff ratios. Therefore, considerable orientation had already occurred in the flowing solution. Further increase of fiber orientation yields a large increase of modulus (from 22 to 67 GPa) during solid‐state deformation (step III). The orientation of the flowing solution was monitored by viscosity and birefringence measurements. The results are discussed in terms of orientation due to elongational and shear flow and, possibly, a flow‐induced transition to a nematic phase in the concentrated solution in which chain entanglement is shown to occur.