2002; Serbian Chemical Society; Volume: 67; Issue: 4 Linguagem: Inglês

10.2298/jsc0204291g

1820-7421

Aleksandar Golubović, Slobodanka Nikolic, Radoš Gajić, Stevan W. Djurić, Andreja Valcic,

Optical and Acousto-Optic Technologies

Y3Al5O12 doped with 0.8%wt.Nd (Nd:YAG) single crystals were grown by the Czochralski technique under an argon atmosphere. The conditions for growing the Nd:YAG single crystals were calculated by using a combination of Reynolds and Grashof numbers. The critical crystal diameter and the critical rate of rotation were calculated from the hydrodynamics of the melt. The crystal diameter Dc=1.5 cm remained constant during the crystal growth while the critical rate of rotation changed from ?c=38 rpm after necking to ?c=13 rpm at the end of the crystal. The value of the rate of crystal growth was experimentally found to be 0.8?1.0 mm/h. According to our previous experiments, it was confirmed that 20 min exposure to conc. H3PO4 at 603 K was suitable for chemical polishing. Also, one-hour exposure to conc. H3PO4 at 493 K was found to be suitable for etching. The lattice parameter a=1.201 (1) nm was determined by X-ray powder diffraction. The obtained results are discussed and compared with published data.