Preparation of Co3O4 nanowires grown on nickel foam with superior electrochemical capacitance
2012; Elsevier BV; Volume: 75; Linguagem: Inglês
10.1016/j.electacta.2012.04.131
ISSN1873-3859
AutoresJichun Huang, Jiangtao Zhu, Kui Cheng, Xu Yang, Dianxue Cao, Guiling Wang,
Tópico(s)Advancements in Battery Materials
ResumoCo3O4 nanowires have been successfully synthesized on nickel foam by a hydrothermal method. The morphology of Co3O4 is examined by scanning and transmission electron microscopy and the phase structure of Co3O4 nanowires is confirmed by X-ray diffraction. The electrochemical capacitance behavior of the Co3O4 nanowires electrode is investigated by cyclic voltammetry, galvanostatic charge/discharge test and electrochemical impedance spectroscopy in 6 mol dm−3 KOH solution. The results show that the Co3O4 nanowires have diameters of around 100 nm and the lengths up to 1–2 μm. The specific capacitance of Co3O4 nanowires is 1019.58 F g−1 at 3.38 A g−1 and 466.06 F g−1 at 33.80 A g−1. The capacitance loss is less than 5% after 1000 charge/discharge cycles at 3.38 A g−1 and with columbic efficiency higher than 98%. The enhancement of pseudocapacitive properties at a higher charging/discharging rate is due to the porous nanostructure and the high utilization of active material.
Referência(s)