Synthesis and characterization of the new delafossite-type oxide CuNi1/3V2/3O2

2004; Elsevier BV; Volume: 7; Issue: 1 Linguagem: Francês

10.1016/j.crci.2003.09.009

1878-1543

Khadija El Ataoui, Jean‐Pierre Doumerc, A. Ammar, Jean‐Claude Grenier, P. Dordor, Michel Pouchard,

Advanced Condensed Matter Physics

Whereas neither delafossite-type CuIVIIIO2 nor CuINiIIIO2 exist, the authors have succeeded in preparing the delafossite oxide CuINiII1/3VIII1/3VIV1/3O2, using classical solid-state reaction. The most probable formal oxidation state for nickel is II, while for vanadium it is a mixed state +III/+IV. The predominant magnetic interactions are antiferromagnetic, but no evidence could be found for long-range ordering. Charge transport results from a hopping process involving V3+ and V4+ cations. As XRD did not reveal any cation ordering, the observed T–1/4-dependence of the electrical conductivity (Mott’s law) is ascribed to a random distribution of the relevant sites. To cite this article: K. El Ataoui et al., C. R. Chimie 7 (2004). Alors que, ni CuIVIIIO2, ni CuINiIIIO2 de type delafossite n’existent, les auteurs ont pu préparer l’oxyde delafossite CuINiII1/3VIII1/3VIV1/3O2, par réaction classique dans l’état solide. Le degré d’oxydation formel le plus probable pour le nickel est II, alors que pour le vanadium il est intermédiaire entre III et IV. Les interactions magnétiques prépondérantes dans cet oxyde sont antiferromagnétiques, mais aucune preuve de l’existence d’un ordre à longue distance n’a été obtenue. Le transport de charges résulte d’un processus de saut impliquant des cations V3+ et V4+. Comme la diffraction X ne révèle aucun ordre cationique, la variation en T–1/4 de la conductivité électrique (loi de Mott) est attribuée à une répartition aléatoire des sites concernés. Pour citer cet article : K. El Ataoui et al., C. R. Chimie 7 (2004).