Mechanism of restored thermoluminescence in lithium fluoride

1977; Wiley; Volume: 44; Issue: 2 Linguagem: Inglês

10.1002/pssa.2210440212

1521-396X

H.-J. Kos, R. Nink,

Ga2O3 and related materials

The dependence of optical absorption and thermoluminescence of LiF crystals on F band bleaching time at different temperatures is used to study the mechanism of “restored” thermoluminescence as applied in thermoluminescence dosimetry. F centers turn out to act as electron sources for refilling of traps. Simultaneously, additional Z2 centers responsible for the TL main peak five are created by the presence of F centers during F band bleaching. The results confirm the close relationship between the 3.3 eV absorption band and the TL pre-peaks. Die Abhängigkeit der optischen Absorption und Thermolumineszenz von LiF-Kristallen von der Dauer der F-Banden-Bleichung bei verschiedenen Temperaturen wird ausgenutzt, um den Mechanismus der „wiederbelebten”︁ Thermolumineszenz zu untersuchen, wie er in der Thermolumineszenz-Dosimetrie angewendet wird. Es zeigt sich, daß F-Zentren die für die Wiederauf-füllung von Haftstellen notwendigen Elektronen liefern. Gleichzeitig werden während der F-Banden Bleichung bei Anwesenheit von F-Zentren zusätzliche Z2-Zentren gebildet, welche das Thermo-lumineszenz-Hauptmaximum fünf verursachen. Die Ergebnisse bestätigen den engen Zusammenhang zwischen der 3,3 eV-Absorptionsbande und den TL-Vormaxima.