Thermodynamic properties of PdFe alloys in the temperature range 1200–1460°C
1962; University of Toronto Press; Volume: 10; Issue: 5 Linguagem: Francês
10.1016/0001-6160(62)90201-8
ISSN1878-0768
Autores Tópico(s)High-Temperature Coating Behaviors
ResumoActivities of Fe in PdFe alloys have been determined from oxidation experiments carried out on alloy samples suspended in a thermal balance. The oxygen potential of the system was increased in small increments at constant temperature by adjusting the composition of the gas phase. Beginning of oxidation of iron in the alloys was observed by an increase in the weight of the samples. The Fe activities of the metal phase were calculated from the known oxygen potential of the atmosphere and the known thermodynamic properties of iron oxides. Les auteurs ont déterminé l'activité du fer dans les alliages PdFe, en utilisant des essais d'oxydation exécutés à l'aide d'une thermobalance. Le potentiel d'oxygène du système était augmenté par petites fractions à température constante en réglant la composition de la phase gazeuse. Le début de l'oxydation du fer se manifestait par un accroissement du poids de l'échantillon. L'activité du fer dans la phase métal était calculée à partir du potentiel d'oxygène de l'atmosphère et des propriétés thermodynamiques des oxydes de fer. Die Aktivitäten von Eisen in PdFe-Legierungen wurden aus Oxydationsversuchen ermittelt, bei denen die Proben an einer thermischen Waage aufgehängt waren. Das Sauerstoffpotential des Systems wurde durch Änderung der Zusammensetzung der Gasphase bei konstant gehaltener Temperatur in kleinen Schritten vergröβert. Eine Gewichtszunahme der Probe zeigte dann den Beginn der Oxydation des Eisens in der Legierung an. Die Eisenaktivitäten der Metallphase wurden aus dem bekannten Sauerstoffpotential der Atmosphäre und den bekannten thermodynamischen Eigenschaften der Eisenoxyde berechnet.
Referência(s)