Hardened Portland blast-furnace slag cement pastes II. The corrosion behavior of steel reinforcement
1975; Elsevier BV; Volume: 5; Issue: 1 Linguagem: Inglês
10.1016/0008-8846(75)90103-9
ISSN1873-3948
AutoresV. K. Gouda, M.A. Shater, R. Sh. Mikhail,
Tópico(s)Innovative concrete reinforcement materials
ResumoThe corrosion behavior of reinforcing steel embedded in various slag cement pastes was studied using the galvanostatic polarization technique. The corrosion resistance is appreciably affected by the degree of fineness of the dry slag cement. In pastes produced from high Blaine area cement, the behavior of embedded steel was very close to that in normal or type I portland cement paste, and is much better than a low Blaine area cement. W/C ratios of 0.25 and 0.40 provided a better passivating medium as compared with W/C ratios of 0.18 and 0.70. Effects of lime or gypsum addition were also investigated and comparatively studied for their action on the corrosion of embedded steel. The results obtained were supported by corrosion rates obtained using the linear polarization technique. Das korrosive Verhalten von Beton-Stahl, das in verschiedenen Hochofen Zementpaste eingesezt ist, wurde durch galvanostatische Polarisationsmethode untersucht. Man fand, dass der korrosive Widerstand von der Teilchengrösse des trockenen Zement abhängig ist: In Zementpaste von einer höheren ausseren Zementoberfläche ist das korrosive Verhalten des Zements hahe zu dieser von Portland-Zement, und besser als das Zement mit kleinerer oberfläche. W/C Verhältniss von 0,25 und 0,4 ergibt ein besseres passives Medium in vergleich zu W/C Verhältniss von 0,18 und 0,7. Der Beeinflussung von Addition von Kalk oder Gips wurde ebenfalls untersucht. Die Ergebnisse wurden durch Untersuchung der Korrosionsgeschwindigkeit mit linearer Polarisations methode weiter befestigt.
Referência(s)