Produção Nacional
Properties of ZrO2–Al2O3 composite as a function of isothermal holding time
2007; Elsevier BV; Volume: 25; Issue: 5-6 Linguagem: Inglês
10.1016/j.ijrmhm.2006.12.005
ISSN0263-4368
AutoresJuliana Kelmy Macário Barboza Daguano, Claudinei dos Santos, Renato Chaves Souza, Roseli Marins Balestra, Kurt Strecker, Carlos Nelson Elias,
Tópico(s)Advanced materials and composites
ResumoZirconia and alumina based ceramics present interesting properties for their application as implants, such as biocompatibility, good fracture resistance, as well as high fracture toughness and hardness. In this work the influence of sintering time on the properties of a ZrO2–Al2O3 composite material, containing 20 wt% of Al2O3, has been investigated. The ceramic composites were obtained by sintering, in air, at 1600 °C for sintering times between 0 and 1440 min. Sintered samples were characterized by microstructure and crystalline phases, as well as by mechanical properties. The grain growth exponents, n, for the ZrO2 and Al2O3 were 2.8 and 4.1, respectively, indicating that different mechanisms are responsible for grain growth of each phase. After sintering at 1600 °C, the material exhibited a dependency of hardness as function of sintering time, with hardness values between 1500 HV (120 min) and 1310 HV (1440 min) and a fracture toughness of 8 MPa m1/2, which makes it suitable for bioapplications, such as dental implants.
Referência(s)