Plastic deformation behavior of β-CuZn single crystals at low and high temperatures

1984; Wiley; Volume: 82; Issue: 1 Linguagem: Inglês

10.1002/pssa.2210820120

1521-396X

Akira Nohara, Marcel Tadashi Izumi, H. Saka, T. Imura,

Advanced ceramic materials synthesis

The orientation and temperature dependences of yield stress and operative slip systems in β-CuZn single crystals with B2 structure are investigated systematically in two deformation modes, i.e. tension and compression, over a wide range of temperature between 77 and 553 K. The results suggest that the stress peak observed around 500 K in β-CuZn cannot be explained easily by mechanisms involving the cross slip of 〈111〉 superlattice screw dislocations onto {110} and/or {112} planes. Es wird die Orientierungs- und Temperaturabhángigkeit der Fließspannung und der aktiven Gleitsysteme in β-CuZn-Einkristallen mit B2-Struktur in zwei Deformationsmoden, d. h. Dehnung und Kompression, über einen weiten Temperaturbereich zwischen 77 und 553 K untersucht. Die Ergebnisse geben Hinweise, daß das bei etwa 500K in β-CuZn beobachtete Fließspannungs-maximum nicht einfach mittels Mechanismen interpretiert werden kann, die Quergleitung von 〈111〉-Superversetzungen auf {110}- oder {112}-Ebenen einschließen.