Growth of off-eutectic composites by zone melting

1971; Taylor & Francis; Volume: 10; Issue: 4 Linguagem: Francês

10.1179/cmq.1971.10.4.273

1879-1395

K. G. Davis, P. Fryzuk,

Aluminum Alloy Microstructure Properties

The use of zone melting for the production of material with composite structure from off-eutectic alloys has been investigated. Lead-tin alloys with composite structure were grown in this way from material with composition up to 10 wt% away from the eutectic. After a short initial region, the composition in the molten zone was eutectic and composite structures with no variation in composition along the bar could be produced. Criteria for the stability of the composite structure were shown to be the same for convective and nonconvective growth. Résumé La production de matériaux à structure composite, a partir d'alliages non-eutectiques droites par la méthode de la zone fondue, a été étudiée. On a ainsi obtenu des alliages plomb-étain à structure composite à partir de mélanges dont la composition différait jusqu'à 10% de celle de l'eutectique. Aprés une zone, au début, la composition dans la zone fondue devint eutectique et on a obtenu des structures composites dont la composition était constante le long du barre au. Les conditions pour la stabilité de la structure, composite sont les mêmes que la croissance ait lieu par convection ou non.