The embrittlement of oxide films on zirconium by neutron irradiation
1967; Elsevier BV; Volume: 21; Issue: 3 Linguagem: Francês
10.1016/0022-3115(67)90182-1
ISSN1873-4820
Autores Tópico(s)Fusion materials and technologies
ResumoAnodic films on zirconium have been irradiated in a nuclear reactor. Cracking between hardness indentations was not reproducible enough to offer a method of detecting embrittlement, but bending tests demonstrated embrittlement between 5 × 1019 and 3 × 1020 nvt (> 1 MeV). Transmission electron microscopy of irradiated stripped film revealed no change in the mode of fracture on a fine scale. It is suggested that embrittlement may be the cause of the enhanced corrosion of zirconium alloys in power reactors. Des films anodiques obtenus sur le zirconium furent irradiés dans un réacteur nucléaire. La fissuration entre empreintes de dureté n'était pas assez reproductible pour offrir une méthode de détection de la fragilité. Mais des essais de flexion révélèrent la fragilité pour des irradiations comprises entre 5 × 1019 et 5 × 1020 nvt (1 MeV). La microscopie électronique par transmission de films détachés du support et irradiés ne révéla aucune modification dans le mode de fracture sur une fine échelle. Il est suggéré que la fragilité peut ê'.ro la cause de la corrosion accrue des alliages de zirconium dans les réacteurs de puissance. Anodische Filme auf Zr wurden in einem Kernreaktor bestrahlt. Risse zwischen Härteeindrücken waren nicht reproduzierbar genug, um eine Methode zur Feststellung der Versprödung anzugeben: Biegeversuche dagegen zeigten, dass eine Versprödung zwischen 5 × 1019 und 5 × 1020 nvt (> 1 MeV) stattfindet. Transmissionselektronenmikroskopie eines bestrahlten und danach entfernten Filmes zeigte in der Bruchart keine Änderung. Es wird angenommen, dass die Versprödung die Ursache bei der steigenden Korrosion von Zr-Legierungen in Leistungsreaktoren ist.
Referência(s)