Transmission electron microscopy of rapidly solidified powders of Ni3Al

1986; Elsevier BV; Volume: 19; Issue: 1 Linguagem: Francês

10.1016/0026-0800(86)90007-8

1878-271X

Ian Baker, J.A. Horton, E. M. Schulson,

Phase-change materials and chalcogenides

Rapidly solidified powders (<100 μm diameter) of stoichiometric Ni3Al and Ni3Al(B,Ti) were examined using transmission electron microscopy. The powders consisted of martensitic dendrites in a Ll2 matrix that contained numerous dislocations. The stoichiometric Ni3Al powder also contained martensitic lamellae between the dendrites. The martensite plates were internally twinned and enriched in aluminum, and probably formed by the transformation of β-NiAl. On a éxaminé sous microscope électronique des poudres (<100 μm de diamétre) rapidement solidifiées de Ni3Al stoichiométriques et Ni3Al(B,Ti). Les poudres consistaient de dendrites martensitiques dans une matrice Ll2 qui contenait de nombreuses dislocations. La poudre de Ni3Al stoichiométrique comportait aussi des lamelles martensitiques entre les dendrites. Les plaques de martensite etaient jumelés intérieurement et enrichies d'aluminum. Il est probable que la martensite s'était formée par la transformation d'une phase β-NiAl qui était la première phase à se solidifier au cours du refroidissement. Schnell härtende Pulver (Durchmesser <100 μm) von stöchiometrischem Ni3Al und Ni3Al(B, Ti) wurden mit Hilfe det Transmissionselektronenmikroskopie untersucht. Die Pulver bestanden aus martensitischen Dendriten in einer Ll2 Matrix., die zahlreiche Verschiebungen enthielten. Das stöchiometrische Ni3Al Pulver enthielt auch martensitische Lamellen zwischen den Dendriten. Die martensitischen Platten waren innen gepaart und mit Aluminum angereichert. Das Martensit wurde wahrscheinlich durch die Transformation der β-NiAl Phase gebildet, die während der Abkühlung als erste Phase erhärtete.