Luminescent properties of Sr2MgSi2O7:Eu2+ as blue phosphor for NUV light-emitting diodes
2010; Elsevier BV; Volume: 204; Issue: 2-3 Linguagem: Inglês
10.1016/j.powtec.2010.08.011
ISSN1873-328X
AutoresXinguo Zhang, Xueping Tang, Jilin Zhang, Huihui Wang, Jianxin Shi, Menglian Gong,
Tópico(s)Advanced Photocatalysis Techniques
ResumoAkermanite phosphor Sr2MgSi2O7:Eu2+ was synthesized by solid-state reaction under a H2–N2 atmosphere, and its photo-physical behaviors were systematically characterized by photoluminescence excitation and emission spectra, concentration quenching, and thermal quenching process. This phosphor is efficiently excited in the wavelength range of 300–420 nm, which matches to a near UV-emitting InGaN chip, and emits strong and wide band blue light peaking at 470 nm. The relationship between emission peak wavelength and Eu2+ occupied sites was illuminated through Van Uitert's equation. The concentration quenching mechanism was verified to be a dipole–dipole interaction and the critical energy-transfer distance was confirmed as around 13 Å through both calculated crystal structure method and experimental spectral method. The activation energy for thermal quenching was calculated to be 0.4044 eV. Phosphor-converted LED was fabricated with Sr2MgSi2O7:0.06Eu2+ and 395 nm-emitting InGaN chip and exhibited strong wide band blue emission. These results indicate that Sr2MgSi2O7:Eu2+ is a promising candidate as a blue component for near UV-based multi-phosphor-converted white LEDs.
Referência(s)