A study of the solidification of argon bubbles in aluminium

1987; University of Toronto Press; Volume: 35; Issue: 10 Linguagem: Francês

10.1016/0001-6160(87)90146-5

1878-0768

R.J. Cox, P.J. Goodhew, John H. Evans,

Scientific Research and Discoveries

A study has been carried out of the solidification of argon in a wide range of argon bubble sizes in aluminium. Using a cryogenic stage samples have been cooled to 78K and the freezing range and lattice parameter of solid argon determined. The results indicate that for very small crystal sizes diffraction from argon will be difficult to detect, at intermediate sizes the argon solidifies epitaxially with the host matrix and for large bubble sizes random crystals may form. Nous avons réalisé une étude de la solidification de l'argon dans l'aluminium, pour un domaine étendu de tailles des bulles d'argon. Nous avons refroidi les échantillons jusqu'à 78K dans un dispositif cryogénique et nous avons déterminé le domaine de solidification et le paramétre réticulaire de l'argon solide. Les résultats montrent que: pour de très petits cristaux, il est difficile de détecter une diffraction de l'argon; pour les tailles intermédiaires, l'argon se solidifie en épitaxie avec la matrice qui l'entoure; pour les grosses bulles, des cristaux orientés au hasard peuvent se former. Die Erstarrung von Argon in Blasen mit Gröβen in einer weiten Spanne in Aluminium wurde untersucht. Mittels einem gekühlten Probenhalter wurden die Proben auf 78 K gekühlt, hierbei wurden der Bereich der Erstarrung und die Gitterparameter des festen Argons bestimmt. Die Ergebnisse weisen darauf hin, daβ sehr kleine Kristalle mittels Beugung sehr schwer zu finden sind, das Argon in mittelgroβen Blasen epitaktisch erstarrt und in groβen Blasen zufällig orientierte Kristalle bildet.