Polymerization stress related to radiant exposure and its effect on microleakage of composite restorations

2007; Elsevier BV; Volume: 35; Issue: 12 Linguagem: Inglês

10.1016/j.jdent.2007.09.009

1879-176X

Fernanda Calabró Calheiros, Fernanda Tranchesi Sadek, Letícia Cristina Cidreira Boaro, Roberto Ruggiero Braga,

Dental Implant Techniques and Outcomes

Verify the influence of radiant exposure (dose) on polymerization stress and microleakage of composite restorations using two adhesive systems.An experimental composite (1BisGMA:1TEGDMA, 75wt.% filler) was subjected to 3, 6, 12 or 24J/cm(2) under 500mW/cm(2). Stress was measured in 1-mm height specimens placed between two glass rods (Ø=5mm) attached to a testing machine. Microleakage was assessed in cylindrical restorations (Ø=5mm, h=2mm) with enamel margins, using Adper Single Bond 2 (SB) or Adper Prompt (PR). After storage, specimens were subjected to dye penetration (50% AgNO(3)) and sectioned twice, perpendicularly. Microleakage of the 8tooth/composite interfaces was recorded in millimeters. KHN was measured at both surfaces of cylindrical specimens (Ø=5mm, 1 or 2mm height). ANOVA/Tukey test were used (alpha=0.05). KHN top and bottom were compared using paired t-tests.Stress increased significantly with dose (3J/cm(2): 1.4+/-0.3(c); 6J/cm(2): 4.3+/-0.5(b); 12J/cm(2): 9.3+/-0.6(a); 24J/cm(2): 9.9+/-0.7(a), in MPa). For both average and maximum microleakage, interactions were not statistically significant (p>0.05). Tooth average microleakage was influenced by the adhesive system (SB<PR) and increased with dose (3J/cm(2)<6J/cm(2)=12J/cm(2)=24J/cm(2)). Tooth maximum microleakage was influenced by dose only (3J/cm(2)<6J/cm(2)=12J/cm(2)=24J/cm(2)). A direct association between stress and microleakage was suggested with SB, while with PR showed severe dye penetration at all doses evaluated. KHN showed significant differences among all groups, except at bottom of 2mm specimens cured with 3 and 6J/cm(2). Differences between top and bottom were found for 2mm specimens cured with 3 and 6J/cm(2).Stress and microleakage increased significantly with the applied radiant exposure.