Octahedral Tilting in MM′X 4 Metal-Oxide Organic Layer Structures

2008; American Chemical Society; Volume: 47; Issue: 11 Linguagem: Inglês

10.1021/ic8000448

ISSN

1520-510X

Autores

M. Vougo-Zanda, Ekaterina V. Anokhina, Selma Duhović, Lumei Liu, Xiqu Wang, Oluwakemi A. Oloba, Thomas A. Albright, Allan J. Jacobson,

Tópico(s)

Magnetism in coordination complexes

Resumo

Three metal-oxide organic frameworks have been synthesized and characterized: vanadium 1,4-benzenedicarboxylate, V2O2F0.6(OH)1.4(BDC).0.4H 2O (1); indium 1,4-benzenedicarboxylate, In 2F2.2(OH)1.8(BDC).1.6H2O (2); and aluminum 1,4-benzenedicarboxylate Al2F3(OH)(BDC) (3). The three-dimensional structures of 1, 2, and 3 have the same framework topology as the previously reported vanadium (III) 1,4-benzenedicarboxylate, VIII2(OH)2F2(BDC). The frameworks consist of inorganic layers constructed from corner sharing ML 6 octahedra (M=V, In, Al and L=OH, F) linked by BDC ligands. The structures are related to a general class of perovskite-related layer structures with composition MM'X4. The layers show characteristic distortions that can be related to tilting of the ML 6 octahedra. In particular the structure of 1 consists of O-V distances that strongly alternate along the b axis. The electronic consequences of this distortion then create a tilting of the 1,4-benzenedicarboxylate ligand about the a axis. Crystal data: 1, orthorhombic, space group Pmna, a=7.101(2) A, b=3.8416(11) A, c=20.570(6) A; 2, orthorhombic, space group Cmcm, a=7.490(4) A, b=21.803(1) A, c=8.154(4) A; 3, monoclinic, space group P2(1)/m, a=10.7569(8) A, b=6.7615(3) A, c=7.1291(3) A, beta=76.02(1) degrees.

Referência(s)
Altmetric
PlumX