Electron diffraction investigation of the AgxTaS2 system. I. Superlattices in Ag1/8TaS2 and Ag2/3TaS2

1982; Wiley; Volume: 71; Issue: 2 Linguagem: Inglês

10.1002/pssa.2210710228

1521-396X

G. A. Scholz, R. F. Frindt, A.E. Curzon,

Crystal Structures and Properties

Superlattices are observed by electron diffraction in electrolytically prepared single crystals of stage 1 Ag2/3TaS2 and stage 2 Ag1/3TaS2 intercalation compounds in the temperature region from 300 to 25 K. These superlattice satellites are explained as ordered silver ion superstructures. The silver ions in both compounds undergo an order-disorder transition in two stages. The first occurs near room temperature and leaves about 25% of the silver ions disordered, which in turn order in the second transition near 90 K. Überstrukturen werden mit Hilfe der Elektronenbeugung in elektrolytisch hergestellten Einkristallen von AgxTaS2 Einlagerungsverbindungen erster Stufe (x = 2/3) und zweiter Stufe (x = 1/3) im Temperaturbereich von 300 bis 25 K beobachtet. Diese Überstruktursatelliten können als geord-nete überstrukturen der Silberionen erklärt werden. Die Silberionen in beiden Verbindungen durchlaufen Ordnungs-Unordnungs-übergänge in zwei Stufen. Der erste kommt bei Raumtem-peratur vor und läßt ungefähr 25% der Silberionen ungeordnet, die sich dann bei einem zweiten übergang bei 90 K ordnen.