Internal friction peak due to hydrogen in copper

1974; Wiley; Volume: 21; Issue: 2 Linguagem: Inglês

10.1002/pssa.2210210224

1521-396X

Maurice Renard, P. Combette, J. Pérez, P. F. Gobin,

Microstructure and mechanical properties

Copper loaded with 5 at ppm hydrogen exhibits an internal friction relaxation peak at 150 K (period of the alternative stress: 2 s). This peak, called PH, can be interpreted as a consequence of the interaction between dislocations and hydrogen atoms and can be described by means of a thermomechanical break-away model. The main features of PH are discussed in connection with cold-work ratio, hydrogen content (in the range 0 to 5 × 10−6), strain amplitude (in the range 10−5 to 10−4), and conditions of growth and annealing. On a mis en évidence un pic de frottement intérieur à 150 K (période de la sollicitation alternative: 2 s) sur du cuivre contenant 5 at ppm d'hydrogène. Ce pic, noté PH, est interprété comme une conséquence de l'interaction entre les dislocations et l'hydrogéne et il est décrit à l'aide d'un modèle de désancrage thermomécanique. On discute les caractéristiques essentielles de PH en liaison avec le taux d'écrouissage, la teneur en hydrogène (entre 0 et 5 × 10−6), l'amplitude de déformation (entre 10−5 et 10−4), et les conditions de croissance et de recuit.