Diffusion of chromium in α-iron

1985; Wiley; Volume: 90; Issue: 2 Linguagem: Inglês

10.1002/pssa.2210900219

1521-396X

Reinhold Braun, Monika Feller‐Kniepmeier,

Magnetic Properties of Alloys

In the temperature range from 915 to 1124 K interdiffusion coefficients in b.c.c. iron-chromium alloys are determined for concentrations up to 28 at% Cr. Above the Curie temperature of pure iron the concentration dependence of the interdiffusion coefficients shows a maximum at 13 at% Cr correlated with the minimum of the solidus line. For lower temperatures the magnetic ordering shifts the maximum to higher concentrations. The transition to magnetic long range order is marked by a discontinuity in the concentration gradient. The temperature minimum in the γ loop is found between 1124 and 1129 K. Der chemische Diffusionskoeffizient des Systems α-Eisen-Chrom wird im Temperaturbereich zwischen 915 und 1124 K fur Chromkonzentrationen von 0 bis 28 at% bestimmt. Oberhalb der Curietemperatur des Eisens zeigt die Konzentrationsabhängigkeit des Diffusionskoeffizienten bei etwa 13 at% Chrom ein Maximum, das durch ein Minimum in der Soliduslinie bedingt ist; für tiefere Temperaturen wird dieses Maximum infolge der magnetischen Ordnung zu höheren Konzentrationen verschoben. Die Einstellung einer magnetischen Fernordnung während der Diffusion ist durch einen Knick im Diffusionsprofil gekennzeichnet. Das Minimum der γ-Schleife liegt zwischen 1124 und 1129 K.