Synthesis of High cis -1,4-BR with Neodymium for the Manufacture of Tires

2016; Hindawi Publishing Corporation; Volume: 2016; Linguagem: Inglês

10.1155/2016/7239540

1687-9430

María Leonor Méndez-Hernández, José Luis Rivera‐Armenta, Ulises Páramo-García, Sergio Corona Galvan, Ricardo García-Alamilla, Beatriz Adriana Salazar-Cruz,

Tribology and Wear Analysis

The salt of neodymium has been widely used in industrial polymerization of 1,3-butadiene. We used the ternary catalytic system neodymium versatate/diethylaluminum chloride/triisobutylaluminum (NdV 3 /DEAC/TIBA) with 0.5 mM NdV 3 /100 g Bd, NdV 3 : DEAC = 1 : 9 mol : mol, and TIBA = 25, 50, 100, and 200 mM. The number-average molecular weight (Mn), weight-average molecular weight (Mw), and polydispersity index (PDI) were analyzed by GPC; the rheological properties were analyzed by DMA. The formulations were prepared with carbon black (IRB6) as reinforcing filler and the mechanical properties were compared to behavior of the different elastomeric compounds. The elastomeric compounds were characterized by their rheological properties, tensile strength, abrasion resistance, tear strength, permanent set, resilience, and fatigue properties. The high cis -1,4 polybutadiene (high cis -1,4-BR) was obtained with a percentage of cis -1,4 ≥97%. The weight-average molecular weight (Mw) was from 150 × 10 3 to 900 × 10 3 g/mol and polydispersity index (PDI) was from 3.1 to 5.1. This work is based on evaluation of the effect of the catalyst system on the final properties of the synthesized polybutadiene.