Thermal treatment effect on physical and mechanical properties of MDF panels

2016; UNIVERSIDADE FEDERAL DE MATO GROSSO; Volume: 4; Issue: 2 Linguagem: Inglês

10.14583/2318-7670.v04n02a03

2318-7670

Rosane Betina Wandscheer, J. Bressan, Rafael Rodolfo de Melo, Dayane Cristina Lima, Talita Dantas Pedrosa, Micheli da Silva Ferreira,

Natural Fiber Reinforced Composites

EFEITO DO TRATAMENTO TERMICO SOBRE AS PROPRIEDADES FISICAS E MECÂNICAS DE PAINEIS MDF O objetivo deste trabalho foi avaliar o efeito do tratamento termico em paineis de MDF, visando principalmente a melhoria de sua estabilidade dimensional. Os paineis foram obtidos junto ao comercio local, fabricados com materia-prima Eucalyptus sp. e resina sintetica ureia-formaldeido. Foram utilizadas vinte e cinco amostras para os ensaios, sendo estas subdivididas em diferentes grupos para o tratamento termico em estufa utilizando as temperaturas de 160 e 180 oC, por um periodo de 6 e 12 min. Juntamente, avaliou-se o desempenho de amostras testemunhas, ou seja, as quais nao foram submetidas a nenhum tipo de tratamento. Apos o tratamento, foram produzidas amostras para os ensaios fisicos (massa especifica, absorcao de agua – as 2 e 24 h, inchamento em espessura, residual e higroscopico – as 2 e 24 h) e mecânicos (flexao estatica e resistencia ao arrancamento de parafusos). Para os ensaios fisicos apos o tratamento, as amostras foram reduzidas as dimensoes de 15 x 15 x 1,5 cm em largura, comprimento e espessura e, para os ensaios mecânicos foram serradas nas dimensoes de 7,5 x 42 x 1,5 cm em largura, comprimento e espessura. Os resultados das propriedades fisicas indicaram que os tratamentos utilizados nao proporcionaram aumento na estabilidade dimensional. As propriedades mecânicas tambem nao foram afetadas pelo tratamento termico. Palavras-chave: paineis de madeira, termorretificacao, estabilidade dimensional ABSTRACT The purpose of this study was to evaluate the effect of heat treatment on MDF panels, aiming mainly to improve their dimensional stability. The panels were obtained from the local market and were manufactured using as raw material Eucalyptus sp. and synthetic urea-formaldehyde resin. Twenty-five samples were used in the tests, which were subdivided into different groups for the thermal treatment in an oven and submitted to temperatures between 160 and 180 °C during a period between 6 and 12 min. We also evaluated the performance of the control samples, i.e., those that have not undergone any treatment. After the treatment, samples were produced for physical tests (density, water absorption - at 2 and 24 h, thickness swelling, residual and hygroscopic swelling - at 2 and 24 h) and mechanical tests (static bending and screw withdrawal resistance). For the physical tests after the treatment, the sample dimensions were reduced to 15 x 15 x 1.5 cm thick, and for the mechanical tests they were sawn in dimensions of 7.5 x 42 x 1.5 cm thick. The results of the physical properties showed that the treatments used did not increase the dimensional stability. The mechanical properties were also not affected by the heat treatment. Keywords : wood panels, thermal rectification, dimensional stability. DOI: http://dx.doi.org/10.14583/2318-7670.v04n02a03