Experimental study on cellulose particulate and its composites
2016; American Institute of Physics; Linguagem: Inglês
10.1063/1.4946730
ISSN1935-0465
Autores Tópico(s)Material Properties and Processing
ResumoAnselme Payen has discovered cellulose after conducting rigorous experiments on wood. In this work an attempt is made to reinforce cellulose particulate into polyester matrix from 1.84 – 9.18 wt % and the lamina is manufactured by JMFIL technique. The fabricated lamina is cut into specimens for various tests as per ASTM standards. Tensile strength of 22.61 MPa is achieved at 1.84 % of cellulose content in composites. Then the cellulose composites at 1.89% of reinforcement level showed 55.57 MPa, 1.86 GPa flexural strength, modulus respectively. ‘C’ kind of failure is visualized for all the specimens and volume fractions during impact test. The cellulose particulate is also analyzed for its morphology, size.