Effect of SiC powder content on lightweight corundum-magnesium aluminate spinel castables
2018; Elsevier BV; Volume: 764; Linguagem: Inglês
10.1016/j.jallcom.2018.06.062
ISSN1873-4669
AutoresZhe Chen, Wen Yan, Stefan Schafföner, Sanbao Ma, Yajie Dai, Nan Li,
Tópico(s)Aluminum Alloys Composites Properties
ResumoThis study investigates five lightweight corundum-magnesium aluminate spinel castables (LCSC) which consisted of porous corundum-spinel aggregates and matrices with 0–2.8 wt% silicon carbide (SiC). The effect of the SiC powder content (SPC) in the matrix on the microstructure, strength, thermal conductivity and slag resistance was analyzed by XRD, SEM and EDS as well as by the thermochemical software FactSage. The addition of SiC powder resulted in a significantly improved interface bonding between the porous aggregates and the matrix enhancing the strength and slag resistance. Whereas the thermal conductivity at 300 °C and 500 °C remained unchanged, it increased significantly at 800 °C and 1000 °C. The optimized LCSC contained 1.9 wt% SiC powder which combined a suitable apparent porosity (32.5%), a low bulk density (2.41 g/cm3), a high flexural strength (17.62 MPa), a high compressive strength (100.76 MPa), a low thermal conductivity (0.978 W/m·K, 1000 °C) and a high slag resistance.
Referência(s)