A mild route for the preparation of calcium carbonate rod bundles in large scale from carbide slag
2021; Institution of Engineering and Technology; Volume: 16; Issue: 3 Linguagem: Inglês
10.1049/mna2.12006
ISSN1750-0443
AutoresBaojun Yang, Zongqi Shao, Dongxue Zhang, Bainian Wang,
Tópico(s)Catalysis and Hydrodesulfurization Studies
ResumoMicro & Nano LettersVolume 16, Issue 3 p. 187-193 ORIGINAL RESEARCH PAPEROpen Access A mild route for the preparation of calcium carbonate rod bundles in large scale from carbide slag Baojun Yang, Baojun Yang School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of ChinaSearch for more papers by this authorZongqi Shao, Zongqi Shao School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of ChinaSearch for more papers by this authorDongxue Zhang, Dongxue Zhang School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of ChinaSearch for more papers by this authorBainian Wang, Corresponding Author Bainian Wang 284855884@163.com orcid.org/0000-0002-0848-5781 School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of China Correspondence Bainian Wang, School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui 230009, People's Republic of China.Search for more papers by this author Baojun Yang, Baojun Yang School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of ChinaSearch for more papers by this authorZongqi Shao, Zongqi Shao School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of ChinaSearch for more papers by this authorDongxue Zhang, Dongxue Zhang School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of ChinaSearch for more papers by this authorBainian Wang, Corresponding Author Bainian Wang 284855884@163.com orcid.org/0000-0002-0848-5781 School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui, 230009 People's Republic of China Correspondence Bainian Wang, School of Chemistry and Chemical Engineering, Hefei University of Technology, No. 193 Tunxi Road, Hefei City, Anhui Province, Hefei, Anhui 230009, People's Republic of China.Search for more papers by this author First published: 20 January 2021 https://doi.org/10.1049/mna2.12006AboutSectionsPDF ToolsRequest permissionExport citationAdd to favoritesTrack citation ShareShare Give accessShare full text accessShare full-text accessPlease review our Terms and Conditions of Use and check box below to share full-text version of article.I have read and accept the Wiley Online Library Terms and Conditions of UseShareable LinkUse the link below to share a full-text version of this article with your friends and colleagues. Learn more.Copy URL Share a linkShare onFacebookTwitterLinked InRedditWechat Abstract In this article, a powerful method to synthesize uniform CaCO3 rod bundles with a high mass fraction of aragonite from carbide slag in large-scale production via a two-step leaching-precipitation process is reported. The effects of the addition of ethylene glycol and reaction temperature on the structure and morphology of the prepared CaCO3 samples were investigated and then demonstrated by the experimental results. It is beneficial to increase the mass fraction of aragonite in CaCO3 samples and ensure the formation of regular rod bundles in morphology when the addition of ethylene glycol is 30 mL and the reaction temperature is 80 °C. The formation mechanism of the CaCO3 rod bundles was preliminarily discussed according to the Muffins–Sekerka theory. 1 INTRODUCTION Industrial solid waste has cascaded detriments on the environment and further sustainable development of mankind, due to the high output and the difficulty of treatment. Carbide slag, as one of the industrial solid wastes on a large scale, is the by-product of the production of acetylene using calcium carbide. As the main component of carbide slag is Ca(OH)2, thus its comprehensive utilization to prepare value-added products, such as CaCO3, has high economic value and environmental protection effects [1-3]. CaCO3 is an industrial filler with excellent performance and low price, which has been widely used in rubber, plastics, coatings, paper, ink, and other industries. CaCO3 has various crystal forms, including calcite, aragonite, and vaterite. As to the aragonite, it is unstable and easy to turn into calcite in nature [4], which belongs to the orthorhombic system and mainly performs as columnar or fibrous morphology, and occasionally dendritic morphology [5]. In recent years, inspired by the biomineralisation process, researches on "controllable synthesis" of CaCO3 have received much more attention. Crystal modifiers, such as organic additives and surfactants, are generally added in the nucleation and growth process to control the morphology and structure of CaCO3 [6-9]. Zheng et al. [10] used the CaCl2 and Na2CO3 as raw materials to synthesize CaCO3 hollow microspheres with calcite and vaterite composite crystal forms by adding polyacrylic acid (PAA) and sodium dodecyl sulphate (SDS) as the crystal control agents. Zhao et al. [11] prepared the conch-like CaCO3 particles from CaCl2 via a liquid-phase precipitation method to using Bi(NO3)3 as an additive. However, the synthesis of CaCO3 with highly regioselective kind of crystalline structure, especially the aragonite, still suffers from lacking strategies. Herein, we described a straightforward way to prepare uniform CaCO3 rod bundles mostly composed of aragonite from carbide slag. The CaCl2 leaching solution was obtained by the chemical reaction between calcium carbide slag and ammonium chloride. Afterward, the CaCl2 was carbonized with Na2CO3 to synthesize aragonite CaCO3 rod bundles in the existence of crystal modifier (ethylene glycol), thus realizing a controllable synthesis of CaCO3 with uniform morphology and particularly crystalline structure under mild conditions. 2 EXPERIMENTAL SECTION Ammonium chloride (NH4Cl, Sinopharm Chemical Reagent Co., Ltd., ≥99%), sodium carbonate (Na2CO3, Sinopharm Chemical Reagent Co., Ltd., ≥99%), ethylene glycol ((CH2OH)2, Sinopharm Chemical Reagent Co., Ltd., ≥99%) were used without any further purification. The carbide slag was provided by CNSG Anhui Hong Sifang Co., Ltd. Figure 1 shows the process flow chart for the preparation of calcium carbonate from carbide slag. In a typical process, 417.5 g of NH4Cl and 338 g of carbide slag were thoroughly mixed in 2000 mL of deionized water via vigorous stir and reacted for 1 h under ambient temperature. The resultant mixture was filtered to obtain a transparent solution containing about 1.5 mol L–1 Ca2+. Afterward, 240 mL of 0.5 mol·L–1 Na2CO3 solution was dropped into the solution consists of 100 mL of the as-obtained Ca2+ solution, 200 mL of deionized water, and 0–40 mL of (CH2OH)2 while stirring (300 rpm) at a constant temperature. After stirring for another 30 min, the precipitate was filtered and washed with deionized water and ethanol, and adequately dried in an oven at 70 °C. The resulting white powders were the calcium carbonate. FIGURE 1Open in figure viewerPowerPoint The synthetic process of calcium carbonate from carbide slag The concentration of Ca2+ in the solution was determined by EDTA complexometric titration. The phase and structure of CaCO3 samples were characterized by X-ray diffraction (XRD, D/max-γB diffractometer, from Japan science corporation, CuKα ray with the tube voltage of 40 kV and current of 100 mA, scanning speed: 4°·min–1 and range: 2θ from 5° to 70°). The morphology of the CaCO3 sample was observed by field emission scanning electron microscope (FESEM, SU8020 electron microscope, from Hitachi, the samples were ultrasonically dispersed for 10 min with ethanol, dropped on the cleaned silicon wafer, then tested with accelerating voltage 15 kV after the surface was sprayed with gold). The microstructure of the sample was observed by a high-resolution electron transmission electron microscope (HRTEM, JEOL-2010 transmission electron microscope, from Nippon electronics, acceleration voltage: 100 kV, dot and stripe resolution: 0.194 and 0.14 nm, respectively). The characteristic groups of the samples were characterized by Fourier transform infrared spectroscopy (FT-IR, Nicolet 67 infrared spectrometer, from Thermo Nicolet, mid-infrared-ATR attenuated total reflection method, scanning wavelength range: 500–4000 cm–1). 3 RESULTS AND DISCUSSION Figure 2 shows the FESEM images of the CaCO3 samples prepared with different addition volumes of ethylene glycol (the concentration of Ca2+: 0.5 mol·L–1, the reaction temperature: 80 °C, and the reaction time: 30 min). FIGURE 2Open in figure viewerPowerPoint FESEM images of the CaCO3 samples obtained with different addition volumes of ethylene glycol. (a) 0 mL; (b) 30 mL The FESEM images in Figure 2 depict that the CaCO3 sample is irregularly granulated without the addition of ethylene glycol (Figure 2(a)). The CaCO3 sample appears as uniform rod bundles with the addition of 30 mL ethylene glycol (Figure 2(b)). Each bundle is grown from a plurality of rod-shaped CaCO3 branches of about 2 μm in length and about 200 nm in diameter, indicating that the addition of ethylene glycol plays a crucial role in modulating the nucleation and growth of CaCO3. Figure 3 shows the XRD pattern of the CaCO3 rod bundles sample. It can be seen from the pattern that the CaCO3 sample is mainly composed of aragonite(a) (PDF 71–2396) and calcite(c) (PDF 85–1108). According to the literature [12], the content of aragonite in the mixed phases can be calculated as follows: y = 1 − 1 1 + 3.9 I A / I C × 100 % (1)where y is the mass fraction of aragonite (%); IA is the strongest diffraction peak (26.27°) intensity of the aragonite, and IC is the strongest diffraction peak (29.48°) intensity of the calcite. According to the Equation (1) and the XRD pattern of the CaCO3 sample, the mass fraction of aragonite is calculated to 94.92%. As listed in Table 1, our synthetic approach could give the highest mass fraction of aragonite among all the reported synthetic approaches till now, indicating the significant advantages of our strategy in the synthesis of CaCO3 with highly regioselective kind of crystalline structure (the aragonite here). FIGURE 3Open in figure viewerPowerPoint XRD pattern of the CaCO3 rod bundles sample TABLE 1. Summary of reported mass fraction of aragonite in the CaCO3 samples Serial number Reaction temperatures / °C Mass fraction of aragonite / % Refs. 1 80 94.9 This work 2 100 93.7 [13] 3 20 82.0 [14] 4 40 80.0 [15] 5 80 70.6 [16] Figure 4 show the high-resolution transmission electron microscope (HRTEM) image and selected area electron diffraction (SAED) diagram of the rod-shaped CaCO3 sample. The clear diffraction spots (Figure 4(b)) and lattice fringes (Figure 4(c)) show that the as-prepared CaCO3 sample is a single-crystalline crystal. The lattice fringe spacing is measured as 0.248 nm, which attributes to the (102) plane of aragonite CaCO3. It is shown that the rod bundles prepared under the experimental conditions preferentially grow along the normal direction of the aragonite CaCO3 crystal plane (102), which is consistent with the indexing results of the diffraction spots in the SAED diagram. FIGURE 4Open in figure viewerPowerPoint TEM and SAED images of CaCO3 rod bundles sample. (a) TEM; (b) SAED; (c) HRTEM Figure 5 is the FT-IR spectra of CaCO3 samples prepared with and without the addition of 30 mL ethylene glycol. The absorption peaks at 1438, 1089, 854, and 713 cm–1 in the spectra corresponding to the antisymmetric and symmetric stretching vibration peak, the out-of-plane, and the in-plane bending vibration peak of CO32–, respectively. Moreover, it is found that the FT-TR spectra of the CaCO3 samples show no characteristic absorption peak for ethylene glycol. The reason might be that ethylene glycol participates in the nucleation and growth process of CaCO3 and plays a crucial role in regulating the formation of CaCO3 rod bundles as demonstrated in Figure 2, however, it may be dissolved in water or ethanol and enter the liquid during the washing process due to its high solubility in water and ethanol. FIGURE 5Open in figure viewerPowerPoint FT-IR spectra of CaCO3 samples prepared with and without the addition of ethylene glycol When the initial concentration of Ca2+ was 0.5 mol·L–1, the reaction temperature was 80 °C, and the reaction time was 30 min, the crystalline structure, and morphologies of the CaCO3 samples prepared with additions of 10, 20, 30, 40, and 50 mL of the ethylene glycol were investigated by XRD and FESEM. The experimental results are shown in Figures 6, 7, and Table 2. FIGURE 6Open in figure viewerPowerPoint XRD patterns of CaCO3 samples prepared with different addition volumes of ethylene glycol FIGURE 7Open in figure viewerPowerPoint FESEM images of CaCO3 samples prepared with different addition. (a) 10 mL; (b) 20 mL; (c) 30 mL; (d) 40 mL TABLE 2. Mass fraction of aragonite in the CaCO3 samples prepared with different addition volumes of ethylene glycol Serial number Addition of ethylene glycol / mL Mass fraction of aragonite / % 1 10 68.77 2 20 73.19 3 30 94.92 4 40 78.64 It can be seen from Figure 6 that the CaCO3 samples prepared with different addition volumes of ethylene glycol are all mixed phases of calcite and aragonite. The mass fraction of aragonite in the sample (Table 2) increases first and then decreases with the increase of the addition of ethylene glycol. When the addition of ethylene glycol is 30 mL, the mass fraction of aragonite reaches the maximum value (94.92%). Figure 7 shows the FESEM images of CaCO3 samples prepared with different addition volumes of ethylene glycol. It can be seen from the images that the addition volume of ethylene glycol has a great influence on the morphology of the prepared CaCO3 sample. When the addition volume of ethylene glycol is less or more than 30 mL (Figure 7(a,b,d)), the CaCO3 sample shows massive or irregular rod-like morphology. When the addition volume of ethylene glycol is 30 mL, the as-prepared CaCO3 sample performs as regular rod bundles (Figure 7(c)). When the initial concentration of Ca2+ was 0.5 mol·L–1, the reaction time was 30 min, and the addition volume of ethylene glycol was 30 mL, the crystalline structure, and morphologies of the prepared samples under different reaction temperatures range from 50 to 90 °C were investigated. The corresponding experimental results are shown in Figures 8, 9, and Table 3. FIGURE 8Open in figure viewerPowerPoint XRD patterns of CaCO3 samples prepared at different reaction temperatures FIGURE 9Open in figure viewerPowerPoint FESEM images of CaCO3 samples prepared at different reaction temperatures. (a) 50 °C; (b) 60 °C; (c) 70 °C; (d) 80 °C; (e) 90 °C TABLE 3. Mass fraction of the aragonite in CaCO3 samples prepared at different temperatures Serial number Reaction temperatures / °C Mass fraction of aragonite / % 1 50 50.79 2 60 82.88 3 70 88.20 4 80 94.92 5 90 95.01 It can be seen from Figure 8 that the CaCO3 samples prepared at different temperatures are all mixed phases of calcite and aragonite. The data in Table 3 shows that the mass fraction of aragonite increases with the increase of reaction temperature. Figure 9 shows the FESEM images of CaCO3 samples prepared at different temperatures. It can be seen from the images that the CaCO3 samples mainly perform as squares or irregular bundles (Figure 9(a,b)) when the reaction temperature is 50 or 60 °C. The CaCO3 sample becomes irregular bundles mixed with rods and block-like structure when the reaction temperature increases to 70 °C. When the reaction temperature is 80 °C, the as-prepared CaCO3 sample performs as regular rod bundles in morphology and exhibits good dispersity (Figure 9(d)). Further increasing the reaction temperature as 90 °C, the CaCO3 sample could keep the regular appearance (Figure 9(e)). As shown in Table 3, the mass fraction of aragonite in the CaCO3 sample is generally increased by elevating the synthetic temperature, but cannot be higher than 95% after increasing the temperature over 80 °C. We herein choose 80 °C as the opportune synthetic temperature to achieve the high mass fraction of aragonite CaCO3 in our system. Combining the above results (Figures 7 and 9, and Tables 2 and 3), it can be clearly seen that the regularity of the CaCO3 rod bundles is positively correlated with the mass fraction of aragonite. When the mass fraction of aragonite is low, the sample mainly performs as block or irregular rod shape. When the mass fraction of aragonite is high, the sample mainly performs as relatively regular rods and rod bundles. These results indicate that the aragonite is apt to grow into rods and rod bundles in morphology (the characteristic morphology of the aragonite is mainly columnar or fibrous [17]) under the experimental condition, and the calcite is apt to form squares in morphology. The addition of ethylene glycol mainly achieves the controllable synthesis of the CaCO3 by regulating the mass fraction of aragonite and calcite in the CaCO3 sample to acquire the rod bundles. It is generally believed that unstable primary polymorphs and amorphous particles form in the early precipitation process and then form the metastable polymorphic structure, and eventually, most of the polymorphic structure is converted into stable calcite structures [18]. In the nucleation process of the CaCO3 rod bundles, due to the amphiphilicity of ethylene glycol, Ca2+ can strongly interact with the hydroxyl groups in the polyhydroxy compound at high temperature, thus reducing the nucleation activation energy of CaCO3 crystal and accelerating the nucleation rate to form large numbers of aragonite nuclei [19, 20]. During the synthetic process, the presence of alcoholic hydroxyl groups in the ethylene glycol generally accelerates the growth rate of CaCO3 crystals while inhibits the conversion of CaCO3 crystals into stable calcites [21]. The introduction of ethylene glycol changes the number of alcoholic hydroxyl groups as well as the viscosity of the reaction system, which has a successive effect on the acceleration of the growth rate of CaCO3 crystal. When the ethylene glycol addition is low, the effect of the alcoholic hydroxyl groups in the system on suppressing the conversion of calcite is limited because of the relatively low concentration, thereby resulting in a high mass fraction of calcite in the CaCO3 sample that performs cuboid structure. An excess of ethylene glycol addition may significantly increase the concentration of hydroxyl groups; however, the as-enhanced viscosity of the system is unfavourable to the growth rate of CaCO3 crystals, which also leads to a high amount of calcite in the CaCO3 samples (Table 2). In this case, elevating the reaction temperature generally decreases the viscosity of the system, thus expediting the growth rate of CaCO3 crystal nuclei due to the accelerated diffusion rate of the system and depressing the conversion of CaCO3 into calcite (Table 3). Herein, an opportune addition of ethylene glycol (30 mL) and a reaction temperature of more than 80 °C in our system is crucial to achieving the successful synthesis of uniform CaCO3 rod bundles. According to a Muffins–Sekerka interface stability theory (MS theory) [22], the driving forces of crystal growth at different orientations and sites lead to the variance in the crystal growth rate when the external conditions are unbalanced. Combining the MS theory for the crystal growth, we proposed a formation mechanism for the CaCO3 rod bundles as shown in Figure 10. Due to the existence of ethylene glycol with high polarity in the aqueous solution, the plane crystal interface of CaCO3 crystal loses the stability followed by the generation of tiny branches at the interfacial convex sites. The uniform CaCO3 rod bundles are eventually formed after the tiny branches grow into CaCO3 rods. FIGURE 10Open in figure viewerPowerPoint Schematic diagram of the formation process of CaCO3 rod bundles 4 CONCLUSION To sum up, we present here the synthesis of CaCO3 rod bundles on a large scale from carbide slag via a straightforward extraction-precipitation process. The ethylene glycol serves as a crystal modifier generally promotes the regioselective growth of CaCO3 crystal from polymorph to mono-crystal, leading to the formation of aragonite with a high mass fraction of more than 94.9%. The facile strategy developed here offers a guideline for the solid waste management and provides an avenue to fabricate other CaCO3 crystal with fine-tuning morphologies and peculiar crystalline structure. Further work might be focused on studying the use of these unique CaCO3 crystals in the fields of catalysis, pharmaceuticals, polymers, paper, inks etc. CONFLICT OF INTEREST The authors declare no conflict of interest. REFERENCES 1Ma, X.T., et al.: CO2 capture performance of cement-modified carbide slag. Korean J. Chem. Eng. 34(2), 580– 587 (2017) CrossrefCASWeb of Science®Google Scholar 2Wang, C., et al.: Preparation of highly dispersed nano calcium carbonate from calcium carbide residue. Chem. Ind. Eng. Prog. 36(S1), 346– 352 (2017) Google Scholar 3Tao, X., et al.: Carbide slag pretreatment enhances volatile fatty acid production in anaerobic fermentation of four grass biomasses. Energ. Convers. Manage. 199 (2019). https://doi.org/10.1016/j.enconman.2019.112009Web of Science®Google Scholar 4Gao, Y.F.: Control of crystalline polymorphs and morphologies for CaCO3 with sodium citrate. M.S. Thesis, South China University of Technology (2015) Google Scholar 5Yan, Z.G.: Studies on the mechanism of the nacre formation of pearl oyster Pinctada fucata. Ph.D. Thesis, Tsinghua University (2008) Google Scholar 6Zhang Z., et al.: High-yield synthesis of vaterite CaCO3 microspheres in ethanol/water structural characterization and formation mechanisms. J Mater. Sci. 50(16), 5540– 5548 (2015) CrossrefCASWeb of Science®Google Scholar 7Yang, M.M., et al.: Investigations of structural phase transformation and THz properties across metal–insulator transition in VO2/Al2O3epitaxial films. Prog. Nat. Sci-Mater. 25(05), 386– 391 (2015) CrossrefCASWeb of Science®Google Scholar 8Ji, X.X., et al.: The synthesis of hollow CaCO3 microspheres in mixed solutions of surfactant and polymer. Mater. Lett. 62(4-5), 751– 754 (2008) CrossrefCASWeb of Science®Google Scholar 9Butler, M.F., et al.: Hollow calcium carbonate microsphere formation in the presence of biopolymers and additives. Cryst. Growth. Des. 9(1), 534– 545 (2009) CrossrefCASWeb of Science®Google Scholar 10Zheng T., Chen X.: Synthesis and formation mechanism of calcium carbonate hollow microspheres. Chem. Ind. Eng. Prog. 36(03), 989– 995 (2017) Google Scholar 11Zhao L.N., Cao Y.: Controllable reparation and fluorescence property of conch-like self-assembled calcium carbonate. Chem. J. Chinese. U. 38(12), 2144– 2148 (2017) Google Scholar 12Wada N., et al.: Effects of divalent cations upon nucleation, growth and transformation of calcium carbonate polymorphs under conditions of double diffusion. J. Cryst. Growth. 148(3), 297– 304 (1995) CrossrefCASWeb of Science®Google Scholar 13Chen, Q.J., et al.: Synthesis and characterization of calcium carbonate whisker from yellow phosphorus slag. Open Chem. 18(1), 347– 356 (2020) CrossrefCASWeb of Science®Google Scholar 14Zhang, J.G., et al.: Aragonite formation induced by open cultures of microbial consortia to heal cracks in concrete: Insights into healing mechanisms and crystal polymorphs. Constr. Build. Mater. (224), 815– 822 (2019) CrossrefWeb of Science®Google Scholar 15Li, L.X., et al.: Mechanism of soluble phosphates effect on synthesis of CaCO3 whiskers. Chinese J. Inorg. Chem. (05), 737– 742 (2008) Google Scholar 16Zhao, L.N., et al.: Biomimetic synthesis of dendrite-shaped aragonite calcium carbonate particles and its application in PVC. Chem. J. Chinese. U., 31(12), 2329– 2333 (2010) CASGoogle Scholar 17Wang, Y.Y.: Biomimetic experimental study of mineralization mechanism of biogenetic calcium carbonate. Ph.D. Thesis, University of Science and Technology of China (2015) Google Scholar 18Yang, Y.N., et al.: Controls of crystal morphology, size and structure in spontaneous precipitation of calcium carbonate. J. Inorg. Mater. 28(12), 1313– 1320 (2013) CrossrefCASWeb of Science®Google Scholar 19Lei, M., et al.: Effects of organic additives on the morphology of calcium carbonate particles in the presence of CTAB. Mater. Lett. 60(9-10), 1261– 1264 (2006) CrossrefCASWeb of Science®Google Scholar 20Yao, Z.J., Chen, T.H.: Influence of temperature on calcium carbonate crystallization in SDBS/glycol/water system. Non-Metallic Mines (6), 8– 10 (2007) Google Scholar 21Manoli, F., Dalas, E.: Spontaneous precipitation of calcium carbonate in the presence of ethanol, isopropanol and diethylene glycol. J. Cryst. Growth 218(2), 359– 364 (2000) CrossrefCASWeb of Science®Google Scholar 22Jie, W.Q.: Principle and Technology of Crystal Growth. Science Press, Beijing (2010) Google Scholar Volume16, Issue34 March 2021Pages 187-193 FiguresReferencesRelatedInformation
Referência(s)