Strain Rate Sensitivity of Polycarbonate and Thermoplastic Polyurethane for Various 3D Printing Temperatures and Layer Heights

2021; Multidisciplinary Digital Publishing Institute; Volume: 13; Issue: 16 Linguagem: Inglês

10.3390/polym13162752

2073-4360

Nectarios Vidakis, Markos Petousis, Apostolos Korlos, Emmanouil Velidakis, Nikolaos Mountakis, Chrisa Charou, Adrian Myftari,

3D Printing in Biomedical Research

In this work, strain rate sensitivity was studied for 3D-printed polycarbonate (PC) and thermoplastic polyurethane (TPU) materials. Specimens were fabricated through fused filament fabrication (FFF) additive manufacturing (AM) technology and were tested at various strain rates. The effects of two FFF process parameters, i.e., nozzle temperature and layer thickness, were also investigated. A wide analysis for the tensile strength (MPa), the tensile modulus of elasticity (MPa), the toughness (MJ/m3) and the strain rate sensitivity index ‘m’ was conducted. Additionally, a morphological analysis was conducted using scanning electron microscopy (SEM) on the side and the fracture area of the specimens. Results from the different strain rates for each material were analyzed, in conjunction with the two FFF parameters tested, to determine their effect on the mechanical response of the two materials. PC and TPU materials exhibited similarities regarding their temperature response at different strain rates, while differences in layer height emerged regarding the appropriate choice for the FFF process. Overall, strain rate had a significant effect on the mechanical response of both materials.