Portal de Periódicos da CAPES

Thermal behaviour of pure and mixed ammonium, molybdate tetrahydrate and aluminum hydroxide

1999; Association of Chemists of the Chemical Institute of Sarria; Volume: 56; Issue: 479 Linguagem: Inglês

2339-9686

W.M. Shaheen, M.M. Selim,

Inorganic and Organometallic Chemistry

espanolEl comportamiento termico del molibdato de amonio tetrahidratado mixto y puro y del hidroxido de aluminio se ha estudiado mediante la tecnica del analisis termico (DTA & TG). Se calcinaban al aire una serie de solidos mixtos y puros a 250-1000o C. Se utilizaba el analisis de difraccion de rayos X para identificar los productos solidos de la calcinacion a distintas temperaturas. Los resultados obtenidos revelaban que el molibdato de amonio tetrahidrato se descompone en MoO3, a aprox. 340o C y luego se funde a aprox. 790o C. Las intensidades de los modelos de difraccion del MoO3 variaban con la temperatura del tratamiento, apuntando a un proceso de orientacion claramente preferido. Por otro lado, el Al(OH)3, se transformaba en un compuesto oxi-hidroxido a aprox. 225o C, despues del cual se podia formar el AI2O3, amorfo. La fase cristalina Al2(MoO4)3 se formaba a 750o C como resultado de la interaccion solido-solido entre los oxidos producidos. El aumento de la temperatura del tratamiento hasta 1000o C llevaba a la descomposicion del compuesto formado AI2(MoO4)3,. La presencia de MoO3 incrementaban la cristalizacion del AI2O3 en la fase alfa, calentando a 1000o C. EnglishThe thermal behavior of pure and mixed ammonium molybdate tetrahydrate and aluminum hydroxide has been studied by thermal analysis (DTA & TG) technique. A series of pure and mixed solids were clacined in air at 250-1 000o C. X-ray diffraction analysis was used to identify the sol id products of calcination at different temperatures. The results obtained revealed that, ammonium molybdate tetrahydrate decomposes to MoO3 at about 340o C and then melts at about 790o C. The intensities of diffraction patterns of MoO3 changed with temperature of treatment pointing to a noticeable preferred orientation process. On the other hand, AI(OH)3 transformed into oxyhydroxide compound at about 225o C after which amorphous AIO3, could be formed. The crystalline phase Al2(MoO4)3 is formed at 750o C as a result of solid-solid interaction between the produced oxides. The increase of temperature of treatment up to 1000o C led to the decomposition of the formed compound Al2(MoO4)3. The presence of MoO3 enhanced the crystallization of AI2O3 in alpha phase upon heating at 1000o C. catalaEstudi del comportament termic del molibdat amonic tetrahidratat pur i en mescla amb hidroxid d'alumini mitjancant tecnica d'analisi termica (DTA & TG). Calcinacio en aire a 250-1000o C d'una serie de solids purs i mesclats i usant l'analisi de difraccio de raigs X s'identificaran els productes solids de la calcinacio a diferents temperatures. Aixi que els resultats obtinguts indiquen que el molibdat amonic tetrahidratat es descompasa a MoO3 a aproximadament 340o C i despres ton aprop de 790 C. Les intensitats deis models de difraccio del MoO3 canvien amb la temperatura de tractament, indicant u proces d'orientacio preferent notable. Per altra banda I'AI(OH), es transforma a oxi-hidroxids prop de 225o C i despres es podia formar AI2O3 amorf. La fase cristal·lina AI2(MO4)3 es forma a 750o C com a consequencia de la interaccio sol id-sol id deis oxids produits. L'augment de la temperatura ·de tractament per sobre els 1000o C produeix la descomposicio del AI2(MoO4)3 format. La presencia de MoO3 mi llora la cristal·litzacio del AI2O3 en fase alfa al calentar per sobre de 1000o C.